This International Standard describes a method of testing ceramic coatings by scratching with a diamond stylus. During a test, either a constant or increasing force normal to the surface under test is applied to the stylus so as to promote adhesive and/or cohesive failure of the coating-substrate system. The test method is suitable for evaluating ceramic coatings up to a thickness of 20 µm and might also be suitable for evaluating other coating types and thicknesses.
The International Standard is intended for use in the macro (1 to 100 N) force range. The procedures may also be applicable to other force ranges. However, appropriate calibration is essential if the normal forces at which failure occurs are to be quantified.
Diese Internationale Norm beschreibt ein Verfahren zur Prüfung keramischer Beschichtungen durch Ritzen mit einem Diamantstift. Bei einer Prüfung wird auf den Stift entweder eine konstante oder zunehmende Kraft senkrecht zur prüfende Oberfläche aufgebracht, um Adhäsions- und/oder Kohäsionsversagen des Systems Schicht/Grundwerkstoff zu begünstigen. Das Prüfverfahren ist für die Bewertung keramischer Schichten mit Dicken bis zu 20 µm geeignet und könnte auch für die Bewertung weiterer Schichtarten und -dicken geeignet sein.
Die Internationale Norm ist für die Anwendung im Makrokraftbereich (1 N bis 100 N) vorgesehen. Die Verfahren dürfen außerdem auf weitere Kraftbereiche angewendet werden. Wenn jedoch die Normalkräfte, bei denen Schichtversagen auftritt, quantitativ bestimmt werden, ist eine geeignete Kalibrierung unerlässlich.