This part of ISO 294 specifies a method of determining the moulding shrinkage and post-moulding shrinkage of
injection-moulded test specimens of thermoplastic material in the directions parallel to and normal to the direction of
melt flow.
For the determination of shrinkage of thermosets see ISO 2577[2].
Moulding shrinkage as defined in this part of ISO 294 excludes the effects of humidity uptake. This is included in
post-moulding shrinkage and thus in total shrinkage. For cases when post-moulding shrinkage is caused by the
uptake of humidity only, see ISO 175[1].
Moulding shrinkage as defined in this part of ISO 294 represents the so-called free shrinkage with unrestricted
deformation of the cooling plates in the mould during the hold period. It may be considered therefore as the maximum
value of any restricted shrinkage.
Dieser Teil von ISO 294 legt ein Verfahren fest für die Bestimmung der Verarbeitungsschwindung und der
Nachschwindung spritzgegossener Probekörper aus Thermoplasten, parallel und senkrecht zur Schmelze-
Fließrichtung.
Hinsichtlich der Bestimmung der Schwindung von Duroplasten siehe ISO 2577 [2].
Die Verarbeitungsschwindung, wie sie in diesem Teil von ISO 294 definiert ist, schließt Auswirkungen von
Feuchteaufnahme aus. Das ist in der Nachschwindung und somit in der Gesamtschwindung enthalten.
Hinsichtlich der Fälle, in denen die Nachschwindung ausschließlich durch Feuchteaufnahme verursacht wird,
siehe ISO 175 [1].
Die Verarbeitungsschwindung, wie sie in diesem Teil von ISO 294 definiert ist, stellt die so genannte freie
Schwindung mit uneingeschränkter Verformung der abkühlenden Formteile im Formwerkzeug während der
Nachdruckzeit dar. Sie kann demzufolge als der Höchstwert einer beschränkten Schwindung angesehen
werden.