This part of IS0 4589 specifies methods for determining the minimum concentration of oxygen, in admixture with nitrogen, that will support combustion of small vertical test specimens under specified test conditions. The results are defined as oxygen index values.
Methods are provided for testing materials that are self-supporting in the form of vertical bars or sheet up to IO,5 mm thick. These methods are suitable for solid, laminated or cellular materials characterized by an apparent density greater than 100 kg/m3. The
methods may also be applicable to some cellular materials having an apparent density of less than 100 kg/m3. A method is provided for testing flexible sheet or film materials while supported vertically.
For comparative purposes, a procedure is provided for determining whether or not the oxygen index of a material lies above some specified minimum value. Oxygen index results obtained using the methods described in this part of IS0 4589 can provide a sensitive
measure of the burning characteristics of materials under certain controlled laboratory conditions, and hence may be useful for quality control purposes. The results obtained are dependent upon the shape, orientation and isolation of the test specimen and the
conditions of ignition. For particular materials or applications,
it may be necessary or appropriate to specify different test conditions. Results obtained from test specimens of differing thickness or by using different ignition procedures may not be comparable and no correlation with flammability behaviour under other
fire conditions is implied. Results obtained in accordance with this part of IS0 4589-2 must not be used to describe or appraise the fire hazard presented by a particular material or shape under actual fire conditions, unless used as one element of a fire risk assessment that takes into account all of the factors pertinent to the assessment of the fire hazard of a parti (...abbreviated)
Dieser Teil von ISO 4589 legt Verfahren zur Bestimmung der minimalen Sauerstoffkonzentration in Gemischen mit Stickstoff fest, bei der die Verbrennung vertikal angeordneter kleiner Probekörper unter festgelegten Prüfbedingungen unterstützt wird. Die Ergebnisse sind als Sauerstoff-Index-Werte definiert. Es werden Verfahren für die Prüfung von Werkstoffen angegeben, die als vertikale Stäbe oder Platten von maximal 10,5 mm Dicke selbsttragend sind. Diese Verfahren sind für feste und mehrschichtige Werkstoffe oder Schaumstoffe mit einer Rohdichte größer als 100 kg/m3 geeignet. Die Verfahren können auch auf einige Schaumstoffe angewendet werden, deren Rohdichte weniger als 100 kg/m3 beträgt. Es wird ein Verfahren zur Prüfung vertikal gehaltener flexibler Platten- oder Folienwerkstoffe beschrieben. Diese konsolidierte Fassung enthält die Änderung A1:2006.