This International Standard specifies a method for the determination
of the reactivity of unsaturated Polyester resins as characterized by the maximum temperature reached by a solution of unsaturated Polyester resin and catalyst when heated in a water-bath at 80 C, by the time taken for the temperature of the mixture to rise from 65 C to this maximum temperature, and also, if the maximum temperature exceeds 90 C, by the time taken for the temperature to rise from 65 to 90 C. These characteristics give an indication of the processing
behaviour of unsaturated Polyester resins and tan be used to compare resins of similar type. As the test results depend very much on the conditions under which the test is carried out, these conditions are described in detail.
Diese Norm beschreibt ein Verfahren zur Bestimmung der Reaktivität von ungesättigten Polyesterharzen in der Weise, daß die Höchsttemperatur einer Lösung von ungesättigten Polyesterharzen und Katalysator erreicht wird, wenn diese in einem Wasserbad bei 80 °C erwärmt wird. Dabei wird die Zeit gemessen, bis die Mischung von 65 °C bis zur Höchsttemperatur gestiegen ist. Wenn die Höchsttemperatur 90 °C übersteigt, wird die Zeit gemessen, bis die Mischung von 65 °C bis 90 °C gestiegen ist. Diese Eigenschaften geben einen Hinweis auf das Verarbeitungsverhalten von ungesättigten Polyesterharzen und können dazu verwendet werden, um Harze ähnlichen Typs miteinander zu vergleichen. Da die Prüfergebnisse sehr von den Bedingungen abhängig sind, unter denen die Prüfung durchgeführt wird, werden diese Bedingungen genau beschrieben.