1 .1 This part of IS0 7765 specifies methods for the determination
of the energy that causes plastics film and sheet less
than I mm in thickness to fail under specified conditions of impact
of a free-falling dart from a specified height that would
result in failure of 50 % of the specimens tested.
1.2 Two methods of test are described.
1.2.1 Method A employs a dart with a 38 mm + I mm
diameter hemispherical head dropped from a height of
066 m + 0,OI m. This method may be used for materials
whose impact resistance requires masses of about 0,05 kg to
about 2 kg to fracture them.
1.2.2 Method B employs a dart with a 50 mm + I mm
diameter hemispherical head dropped from a height of
I ,50 m + 0,OI m. Its range of applicability is from about 0,3 kg
to about 2 kg.
1.3 The measurement technique is the staircase method. A
uniform missile mass increment is employed during testing and
the missile weight is decreased or increased by the uniform increment
after test of each specimen, depending upon the result
(failure or no failure) observed for the specimen.
Diese Norm enthält die Beschreibung von Verfahren zur Bestimmung der Energie, die zum Bruch von Kunststoff-Folien oder Filmen mit einer Dicke unter 1 mm führt. Dazu dient ein aus vorgeschriebener Höhe frei fallender Schlagkopf, dessen Masse so zu variieren ist, dass 50 % der Prüfkörper bei der Prüfung durchschlagen werden. Es werden zwei Verfahren beschrieben. Bei Verfahren A wird ein Schlagkopf mit 38 mm Durchmesser der halbkugelförmigen Spitze und einer Höhe von 0,66 m benutzt, und bei Verfahren B ein halbkugelförmiger Schlagkopf mit 50 mm Durchmesser und einer Höhe von 1,5 m. Die Messung erfolgt nach einer Stufentechnik.