This document specifies a comparative method for determining the flow characteristic of a fused thermosetting coating powder down a plane inclined at a set angle to the horizontal.
The aim of the test method described in this document gives an indication of the degree of melt flow that can occur during the curing of the coating powder. This characteristic contributes to the surface appearance and to the degree of coverage over sharp edges.
The test is a comparative method for checking for batch to batch variation in the behaviour of a given coating powder. Correlation between the results from coating powders of differing composition is not to be expected.
This method is not suitable for coating powders which have gel times of less than 1 min at the test temperature when characterised according to ISO 8130-6. This method is also not suitable for textured powders.
Dieses Dokument legt ein vergleichendes Verfahren zum Bestimmen der Fließeigenschaften eines geschmolzenen wärmehärtenden Pulverlackes entlang einer Ebene, die in einem festgelegten Winkel zur Waagerechten geneigt ist, fest.
Das Ergebnis des in diesem Dokument beschriebenen Prüfverfahrens gibt einen Hinweis auf den Grad des Schmelzflusses, der beim Härten von Pulverlacken auftreten kann. Diese Kenngröße wirkt sich auf das Aussehen der Oberfläche und den Grad der Abdeckung über scharfen Kanten aus.
Die Prüfung ist ein vergleichendes Verfahren und dient zur Kontrolle des Verhaltens eines bestimmten Pulverlackes auf Unterschiede von Charge zu Charge. Bei Pulverlacken mit unterschiedlicher Zusammensetzung ist eine Korrelation der Ergebnisse nicht zu erwarten.
Das Verfahren ist nicht bei Pulverlacken, die nach ISO 8130-6 kürzere Gelzeiten als 1 min bei der Prüftemperatur aufweisen, anwendbar. Das Verfahren ist ebenfalls nicht auf Strukturpulver anwendbar.