1.1 This part of ISO 899 specifies a method for determining the flexural creep of plastics in the form of
standard test specimens under specified conditions such as those of pretreatment, temperature and humidity.
It applies only to a simple freely supported beam loaded at mid-span (three-point-loading test).
1.2 The method is suitable for use with rigid and semi-rigid non-reinforced, filled and fibre-reinforced
plastics materials (see ISO 472 for definitions) in the form of dumb-bell-shaped test specimens moulded
directly or machined from sheets or moulded articles.
NOTE The method may be unsuitable for certain fibre-reinforced materials due to differences in fibre orientation.
1.3 The method is intended to provide data for engineering-design and research and development
purposes. Data for engineering-design purposes requires the use of extensometers to measure the gauge
length of the specimen. Data for research or quality-control purposes may use the change in distance
between the grips (nominal extension).
1.4 Flexural creep may vary significantly with differences in specimen preparation and dimensions and in
the test environment. The thermal history of the test specimen can also have profound effects on its creep
behaviour (see Annex A). Consequently, when precise comparative results are required, these factors must
be carefully controlled.
1.5 If flexural-creep properties are to be used for engineering-design purposes, the plastics materials
should be tested over a broad range of stresses, times and environmental conditions.
1.6 The method may not be suitable for determining the flexural creep of rigid cellular plastics (attention is
drawn in this respect to ISO 1209-1, Cellular plastics, rigid ¿ Flexural tests ¿ Part 1: Bending test, and
ISO 1209-2, Cellular plastics, rigid ¿ Flexural tests ¿ Part 2: Determination of flexural properties).
Diese Norm legt eine Methode zur Bestimmung des Kriechverhaltens von Kunststoffen unter Biegebeanspruchung fest. Es werden Standardprobekörper unter festgelegten Bedingungen von Vorbehandlung, Temperatur und Feuchtigkeit verwendet. Dieser Teil bezieht sich nur auf einen einfachen, frei aufgelegten Biegebalken, der in der Mitte belastet ist (Dreipunkt-Biegeversuch). Die Methode ist geeignet für steife und halbsteife unverstärkte, gefüllte und faserverstärkte Kunststoff-Formmassen. Es werden stabförmige, prismatisch Probekörper verwendet, die entweder direkt gespritzt oder spanend aus Platten oder gespritzten Fertigteilen entnommen wurden. Anmerkung: Die Methode kann für bestimmte faserverstärkte Kunststoffe wegen Unterschieden in der Faserorientierung ungeeignet sein.