1.1 This part of ISO 5659 specifies a method of measuring smoke production from the exposed surface of
specimens of essentially flat materials, composites or assemblies not exceeding 25 mm in thickness when
placed in a horizontal orientation and subjected to specified levels of thermal irradiance in a closed cabinet
with or without the application of a pilot flame. This method of test is applicable to all plastics and may also be
used for the evaluation of other materials (e.g. rubbers, textile-coverings, painted surfaces, wood and other
materials).
1.2 It is intended that the values of optical density determined by this test be taken as specific to the
specimen or assembly material in the form and thickness tested, and are not to be considered inherent,
fundamental, properties.
1.3 The test is intended primarily for use in research and development and in fire safety engineering of
buildings, trains, ships, etc., and not as a basis for ratings for building codes or other purposes. No basis is
provided for predicting the density of smoke that may be generated by the materials upon exposure to heat
and flame under other (actual) exposure conditions, nor is any correlation established with measurements
derived from other test methods. This test procedure excludes the effect of irritants on the eye.
NOTE This test procedure addresses the loss of visibility due to smoke density, which generally is not related to
irritancy potency, as explained in Part 1 of this International Standard.
1.4 It is emphasized that smoke production from a material varies according to the irradiance level to which
the specimen is exposed. In making use of the results of this method, it should be borne in mind that the
results are based on exposure to the specific irradiance levels of 25 kW/m2 and 50 kW/m2.
Dieser Teil der Norm legt ein Verfahren zur Messung des Rauches fest, der auf der Oberfläche von Probekörpern entsteht, wenn im wesentlichen flache Werkstoffe, Verbundstoffe oder vorgefertigte Teile mit einer Dicke von höchstens 25 mm horizontal angeordnet und in einer geschlossenen Prüfkammer mit oder ohne Anwendung einer Zündflamme einer Wärmebestrahlung mit einer bestimmten Intensität ausgesetzt werden. Dieses Prüfverfahren gilt für alle Kunststoffe und darf auch zur Bewertung anderer Werkstoffe (zB Gummi, textile Abdeckungen, Flächen mit Farbanstrichen, Holz und andere Baustoffe) angewendet werden. Die Werte stellen keine werkstoffspezifischen, grundlegenden Eigenschaften dar. Die Prüfung ist für die Anwendung in Forschung und Entwicklung und nicht in erster Linie als Bewertungsgrundlage für Bauvorschriften oder sonstige Anwendungen bestimmt.